Block copolymer compositions

ABSTRACT

Block copolymer compositions having improved adhesion to porous substrates are prepared by employing an anionic polyarene as a component instead of a free radical polymerized polyarene. Also disclosed is a process for simultaneously preparing the block copolymer and anionic polyarene.

BACKGROUND OF THE INVENTION

The use of certain block copolymers and their compounds in a number ofend-uses and especially in footwear, is rapidly expanding. For example,in the footwear industry, certain block copolymer compounds are beingused in large volume in the manufacture of a wide variety of shoesincluding canvas shoes, sport shoes, and dress shoes. The blockcopolymers may be utilized for this purpose for soling, foxing,,innersoles and the like. These compositions are disclosed in Hendrickset al, U.S. Re. Pat. No. 28,236. In general, those shoe componentcompositions usually comprise a mixture of block copolymer, extendingoil, polystyrene and possibly a filler. Many other end-uses of blockcopolymers are known, such as in pharmaceutical applications, sportswearand other artifacts. For the most part, these block copolymers haveproved to be particularly advantageous in many respects, includingflexibility, processability, lack of vulcanization requirement and wetslip. However, in certan respects, shortcomings have been noted. Forexample, commercial compounds should be free from delamination, freefrom elephant hide, and free from flow markings and marring. Withrespect fo footwear, one of the major shortcomings of the blockcopolymer compounds such as those referred to in U.S. Re. 28,236 is thelack of adhesion of the compounds to the shoe upper. A new compositionhas been found that greatly improves the adhesive characteristics of theblock copolymer compound.

SUMMARY OF THE INVENTION

The present invention is a composition suitable for footwearapplications comprising:

    ______________________________________                                                                Parts                                                                         by Weight                                             ______________________________________                                        (a) a block copolymer havng at least                                              two monoalkenyl arene polymer blocks                                          A and at least one elastomeric con-                                                                         100                                             jugated diene block B, said blocks A                                          comprising 8 - 65% by weight of the                                           copolymer;                                                                (b) a polyarene produced by the anionic                                           polymerization of a monoalkenyl arene;                                                                      5 - 125                                     (c) a hydrocarbon rubber extending oil; and                                                                     5 - 175                                     (d) a finely divided filler.      0 - 120                                     ______________________________________                                    

Shoe soles made according to the above formulation exhibit improvedadhesion to shoe uppers in addition to improved mold cycle time, reducedmarring, and improved cut growth.

In a further embodiment, it is preferred that the ratio of the numberaverage molecular weight of the polyarene divided by the number averagemolecular weight of the A block of the block copolymer be between about0.6 and about 2.0, preferably between about 0.8 and about 1.5. As shownin the following embodiments, when the molecular weights of polyareneand the A blocks are about equal, the adhesive characteristics of theblend are greatly improved. While the exact reason for this surprisingimprovement is not known, it is likely that these matching molecularweights result in improved compatibility of the polymers and reducedchances for segregation of polyarene particles on the surface of theblend.

Further, it is also preferred that the Q value of the polyarene, definedas the ratio of the weight average molecular weight over the numberaverage molecular weight be between about 1.0 and about 3.0, preferablybetween about 1.0 and 2.0. The Q value for most crystal grade thermalpolystyrene produced by the typical free-radical process is over about5.0.

Also disclosed is a process for simultaneously forming the blockcopolymers and anionic polystyrene components employed in thecomposition which process comprises:

(a) polymerizing a monoalkenyl arene in a solvent and in the presence ofa lithium alkyl initiator to form a living precursor polymer of thearene;

(b) adding less than the stoichiometric amount of terminating agentrequired to terminate all lithium ions wherein at least a portion of theremaining precursor arene polymer blocks contains living lithium ions,therein forming terminated block polymers of anionic polyarenes;

(c) polymerizing a conjugated diene in the presence of the remainingliving precursor arene blocks therein forming a living two blockpolymer;

(d) contacting said living two block polymer with a coupling agenttherein forming a coupled block copolymer; and

(e) recovering the coupled block copolymer and the anionic polyareneblocks.

When the block copolymer and the anionic polyarene are preparedsimultaneously there are a number of advantages. For one, the molecularweights of the polyarene blocks in the block copolymer and the anionicpolyarene homopolymer are similar. In addition, the two components arerecovered from the solution together and the usual problem of obtaininguniform mixing of the polyarene and block copolymer is eliminated.

DETAILED DESCRIPTION OF THE INVENTION

The block copolymers employed in the present composition arethermoplatic elastomers and have at least two monoalkenyl arene polymerend blocks A and at least one elastomeric conjugated diene polymer midblock B. The number of blocks in the block copolymer is not of specialimportance and the macromolecular configuraion may be linear, graft orradial (branched) depending upon the method by which the block copolymeris formed. Much preferred is a radial block copolymer. Typical blockcopolymers of the most simple configuration would have the structurepolystyrene-polyisoprene-polystyrene andpolystyrene-polybutadiene-polystyrene. A typical radial polymer wouldcomprise one in which the diene block has three or more branches, thetip of each branch being connected to a polystyrene block. See U.S.3,594,452. Expressed another way, the invention also contemplates (butis not limited to) the use of configurations such as A--B--(B--A)_(n)where n varies from 1 to 15. Other useful monoalkenyl arenes from whichthe thermoplastic (non-elastomeric) blocks may be formed includealphamethyl styrene, tert-butyl styrene and other ring alkylatedstyrenes as well as mixtures of the same. The conjugated diene monomerpreferably has 4 to 5 carbon atoms such as butadiene and isoprene.

The average molecular weights of each of the blocks may be varied asdesired. The monoalkenyl arene polymer blocks preferably have numberaverage molecular weights between about 5,000 and about 125,000, morepreferably between about 15,000 and about 100,000. The elastomericconjugated diene polymer blocks preferably have number average molecularweights between about 15,000 and about 250,000, more preferably betweenabout 25,000 and about 150,000. The average molecular weights of thepolystyrene end blocks are determined by gel permeation chromotography,whereas the polystyrene content of the polymer is measured by infaredspectroscopy of the finished block polymer. The weight percentage of thethermoplastic monoalkenyl arene blocks in the finished block polymershould be between about 8 and 65%, preferably between about 30% andabout 50% by weight. The general type and preparation of these blockcopolymers are described in U.S. Re. Pat. No. 28,246 and in many otherU.S. and foreign patents.

The block copolymers useful in the composition of this invention mayalso be hydrogenated either selectively, randomly or completely.Selected conditions may be emloyed, for example, to hydrogenate theelastomeric diene center block while not so modifying the monoalkenylarene polymer blocks. Two examples of hydrogenated polymers arepolyvinylcyclohexane-hydrogenated polyisoprene-polyvinyl-cylohexane andpolystyrene-hydrogenated polybutadiene-polystyrene. Preferably, blocks Aare characterized in that no more than about 25% of the originalaromatic double bonds are reduced by hydrogenation while blocks B arecharacterized by having at least 75% of the aliphatic double bondsreduced by hydrogenation. See generally U.S. Pat. No. 3,595,942.

The polystyrene commonly employed in prior art formulations for footwearis typically termed "crystal grade polystyrene". This prior art crystalgrade polystyrene is commercially produced almost exclusively by freeradical polymerization. See Teach, Kiessling, Polystyrene, ReinholdPublishing Corp., Page 38 (1960). The catalyst employed in the freeradical polymerization step is usually an organic peroxide. The presentinvention employs a homopolymer of a monoalkenyl arene prepared bysolution polymerization or mass polymerization with an organomonolithiuminitiator. -phenylbutyllithium,

A method for producing the anionic polyarene by a mass polymerizationprocess in the absence of solvent is disclosed in U.S. Pat. No.3,790,547. However, the preferred method for producing the anionicpolyarene is by a solution polymerization process similar to thatemployed in making the block copolymers of the instant invention.

A much preferred method for producing the anionic polyarene is tosimultaneously manufacture the polyarene and the block copolymer. Thefirst step of this process involves contacting the monoalkenyl arene andthe organomonolithium compound (initiator) in the presence of an inertdiluent therein forming a living polymer compound having the simplifiedstructure A-Li. The monoalkenyl arene is preferably styrene. Otheruseful monoalkenyl arenes from which the thermoplastic (non-elastomeric)blocks may be formed include alphamethyl styrene, tert-butyl styrene andother ring alkylated styrenes as well as mixtures of the same. The inertdiluent may be an aromatic or naphthenic hydrocarbon, e.g., benzene orcyclohexane, which may be modified by the presence of an alkene oralkane such as pentenes or pentanes. Specific examples of suitablediluents include n-pentane, n-hexane isooctane, cyclohexane, toluene,benzene, xylene and the like. The organomonolithium compounds(initiators) that are reacted with he polymerizable additive in step oneof this invention are represented by the formula RLi; wherein R is analiphatic, cycloaliphatic, or aromatic radical, or combinations thereof,preferably containing from 2 to 20 carbon atoms per molecule. Exemplaryof these organomonolithium compounds are ethyllithium, n-propyllithium,isopropyllithium, n-butyllithium, sec-butyllithium, tert-octyllithium,n-decyllithium, n-eicosyllithium, phenyllithium, 2-naphthyllithium,4-butylphenyllithium, 4-tolyllithium, 4-phenylbutylthium,cyclohexyllithium, 3,5-di-n-hepthylcyclohexyllithium,4-cyclopentylbutyllithium, and the like. The alkyllithium compounds arepreferred for employment according to this invention, especially thosewherein the alkyl group contains from 3 to 10 carbon atoms. A muchpreferred initiator is sec-butyllithium. See U.S. Pat. No. 3,231,635.The concentration of the initiator can be regulated to control molecularweight, Generally, the initiator concentration is in the range of about0.25 to 50 millimoles per 100 grams of monomer although both higher andlower initiator levels can be used if desired. The required initiatorlevel frequently depend upon the solubility of the initiator in thehydrocarbon diluent. These polymerization reactions are usually carriedout at a temperature in the range of -60° to +300° F and at pressureswhich are sufficient to maintain the reaction mixture in the liquidphase.

In the next step, less than the stoichiometric amount of terminatingagent required to remove all lithium radicals is added to the solution.This results in the formation of the anionic polyarene block polymers ofthe instant invention. There will remain in the solution, however,living polymer blocks of the structure A-Li. Typical terminating agentsare water or alcohols.

Next, this living polymer in solution is contacted with a conjugateddiene. Preferred dienes include butadiene and isoprene. The resultingliving polymer has a simplified structure A-B-Li. It is at this pointthat the living polymer is coupled.

There are a wide variety of coupling agents that can be employed. Anypolyfunctional coupling agent which contains at least two reactive sitescan be employed. Examples of the types of compounds which can be usedinclude the polyepoxides, polyisocyanates, polyimines, polyaldehydes,polyketones, polyanhydrides, polyesters, polyhalides, polyvinylbenzenes, and groups such as the combination of epoxy and aldehydegroups, isocyanate and halide groups, and the like. Various othersubstituents which are inert in the treating reaction can be presentsuch as hydrocarbon radical as exemplified by the alkyl, cycloalkyl,aryl, aralkyl, and alkaryl groups and the alkoxy, aryloxy, alkylthio,arylthio, and teritary amino groups. Many suitable types of thesepolyfunctional compounds have been described in U.S. Pat. No. 3,595,941;3,468,972; 3,135,716; 3,078,254; 3,985,830; and 3,594,452. When thecoupling agent has two reactive sites such as dibromoethane, the polymerwill have a linear ABA structure. When the coupling agent has three ormore reactive sites, such as silicon tetrachloride, the polymer willhave a branched structure, such as (AB)_(n) BA. Divinyl benzene resultsin a star polymer having a large number of arms, e.g. 7-15 arms.

The typical coupling conditions include a temperature of between about50° and about 170° F, and sufficient pressure to maintain the reactantsin a liquid phase.

Instead of employing a coupling reaction, it is also within the scope ofthe instant invention to employ a sequential process, such as thatdisclosed in U.S. Pat. No. 3,231,635, to form a linear ABA-type polymer.In that case, instead of adding a coupling agent to an AB-Li livingpolymer, additional monoalkenyl arene monomer is added to the solutiontherein resulting in the formation of an ABA-Li polymer.

Following the coupling reaction or the completion of the sequentialprocess, the product is neutralized such as by the addition ofterminators, e.g. water, alcohol or other reagents, for the purpose ofremoving the lithium radical forming the nucleus for the condensedpolymer product. The product is then recovered such as by coagulationutilizing hot water or steam or both. A typical recovery process isdisclosed in U.S. Pat. No. 3,804,145.

The amount of anionic polyarene employed in the compositions of theinstant invention varies from about 5-125 phr, preferably about 20-90phr. The term "phr" is well known and means parts by weight per 100parts by weight rubber (or block copolymer as in the present case).

The hydrocarbon rubber extending oils, usually referred to asparaffinic/naphthenic oils, are usually fractions of refined petroleumproducts having less than about 30% by weight of aromatics (by claygelanalysis) and usually have viscosities between about 100 and 500 SSU at100° F. Commercial extending oils include SHELLFLEX® oils, Nos. 310, 371and 372 (which is a blend of 310 and 371. The amount of extending oilemployed varies from about 5-175 phr preferably from about 50-125 phr.

Additional resins may also be employed in the present compositions. Theadditional resins employed herein are flow promoting resins that arecompatible with the monoalkenyl end blocks of the block copolymer andinclude polymers of alphamethyl styrene, copolymers of alphamethylstyrene and vinyltoluene coumarone-indene resins, polyindene resins,poly(methyl indene) resins and polystyrene resins of low molecularweight for flow promotion. The amount of end block compatible resinemployed varies from about 0-150 phr, preferably 5-50 phr.

The fillers used in the present compositons are well known in the artand include clay, talc, silica, titanium dioxide, carbon blacks, calciumcarbonate, and other pigments as well as fibrous fillers such ascellulosic fibers, sawdust, ground cork, etc. Preferred fillers includeclay and calcium carbonate. The amount of filler employed varies from0-250 phr, preferably 5-60 phr. Additional minor amounts ofantioxidants, ultra-violet stabilizers and the like may also be added.

The components of this invention may be combined by processes known inthe art including blending such as by extrusion, Banbury mixing or bydry-blending procedures. In the latter case, it is preferred that theblock copolymer and polyarene be formed or ground in particles having anaverage size less than about 4 millimeter diameter onto which theextending oil is absorbed. Following this, the remaining powderedcomponents may be added and vigorously dry-blended therewith such as inwell-known dry-blending equipment long used in the PVC dry-blending art.

While the present specification emphasizes the use of these compositionsin footwear components, other end-uses also are contemplated. Theseinclude, for example, automotive parts and wire and cable coatings. Thepresent compositions, when utilized as coatings, result in wire andcable products which can be tightly bent or coiled without buckling ofthe coating. Tubular products such as hoses and the like also arecontemplated.

The use of the present composition in footwear includes especially theiruse in soling when prepared by injection molding and slab soling, suchas produced by cutting shoe sole forms from extruded slab-stock. Theadvantages of the present compositions are most apparent in injectionmolding of unit soles which are later attached by adhesion or sewing touppers. In this situation, it has been found that the unit soles arereadily removed from the injection mold and have reduced weld lineformation on the surface. Furthermore, the sole so produced is resistantto delamination, has a relatively low abrasion loss, exhibits virtuallyno elephant hide, and has improved adhesion to the shoe upper. Theseunit soles (which term refers in the trade to a sole including anintegral heel portion) are useful both as a leather replacement and asan improvement over the prior art vinyl soles. The compositions also maybe used in the manufacture of injection molded canvas shoe soles whereinthe soling is directly injection molded onto the canvas upper.

The invention is further illustrated by means of the followingillustrative embodiment, which is given for the purpose of illustrationalone and is not meant to limit the invention to the particularreactants and amounts disclosed.

Illustrative Embodiment I

In Illustrative Embodiment I, various compositions were prepared usingboth crystal grade polystyrene and anionic polystyrene. In allcompounds, the block copolymer was a styrene-butadiene branched blockcopolymer havin polystyrene blocks with number average molecular weightsof about 30,000. Also in each compound, the extending oil was aparaffinic oil (SHELLFLEX® 311) and the additive package included 0.6parts KEMAMIDE E® (an erucamide), 0.5 parts DLTDP(dilaurylthiodipropionate), 0.5 parts IRGANOX® 1010 (antioxidant coveredby U.S. Pat. Nos. 3,285,855 and 3,644,482), and 1.5 parts EPON® 1004resin (an epichlorohydrin/bisphenol A-type solid epoxy resin).

The crystal grade polystyrene was Amoco 303 TJ thermal producedpolystyrene by a peroxide catalyzed free-radical process, and had aweight average molecular weight (M_(w)) of about 230,000 and a numberaverage molecular weight (M_(n)) of about 48,000. Accordingly, the ratioof M_(w) /M_(n) = 5.2 = Q.

Various anionic polystyrenes were prepared by polymerizing styrene in acyclohexane solvent with a sec-butyl lithium initiator. These polymershad varying number average molecular weight, and a Q value of about 1.1.

The individual components were mixed on a Banbury Mixer at about 300° Ffor a total mix time of about 3 minutes.

Samples of the various compositions were tested according to thefollowing tests:

    ______________________________________                                                           Standard                                                   Test               Test Number                                                ______________________________________                                        Shore A Hardness   D-2240                                                     Tinius Olsen Stiffness                                                                           D-747                                                      Taber Abrasion     D-1044                                                     Ross cut growth    D-1052                                                     Adhesive peel      Standard footwear test                                     Trouser tear       Standard footwear test                                     ______________________________________                                    

In addition, the various compositions were used in the injection moldingof unit soles in a unit sole mold attached to a Desma rotating table andinjection molded by a Monopak molding machine. The pulling forcerequired to remove the unit soles from the mold were noted for variouscomposition.

The various formulations and test results are presented below in TableI.

                                      Table I                                     __________________________________________________________________________     Composition, Parts by Weight                                                                   1      2      3      4      5                               __________________________________________________________________________    Block Copolymer   100    100    100    100    100                             Extending Oil     100    100    100    100    100                             Crystal Polystyrene                                                                             55     --     --     --     --                              Anionic Polystyrene                                                                             --     55     55     55     55                              Number average mol. wt.                                                                         --     (10m)  (30m)  (41m)  (55m)                           (m = 1000)                                                                    Additive Package  4.1    4.1    4.1    4.1    4.1                             Total Parts       259.1  259.1  259.1  259.1  259.1                           Specific Gravity  0.953  0.953  0.954  0.954  0.954                           Test Results                                                                  Shore A Hardness  48/45  80/76  60/55  52/48  48/45                           (compression molded)                                                          Instant /10 sec.                                                              Shore A Hardness  67/62  90/85  82/76  74/68  69/63                           (injection molded)                                                            Instant /10 sec.                                                              Taber Abrasion, cc loss/kc                                                                      0.3175 0.3004 0.2682 0.2138 0.2077                          Tinius Olsen Stiffness, PSI                                                                     1841   5000   4270   2607   1869                            Pulling Force during demolding, lbs                                                             9.4    10.3   5.8    5.3    5.1                             Adhesive Peel, PLI                                                                              54     75     91     82     80                              Ross Flex Cut Growth, flexes to                                                                 300m   310m   750m   860m   730m                            500% growth                                                                   Trouser Tear, lbs per linear                                                                    145/154                                                                              231/228                                                                              217/221                                                                              215/228                                                                              207/210                         inch (normal/parallel)                                                        __________________________________________________________________________

As can be seen above, compositions employing anionic polystyrene inplace of crystal grade polystyrene exhibited markedly improved adhesionproperties, better abrasion resistance, easier demolding and greaterhardness and stiffness. In addition, the molded unit soles were morefree of weld lines, had less elephant hide, showed no delaminationtendencies and were more resistant to surface marring.

What is claimed is:
 1. A polymeric composition comprising:

    ______________________________________                                                                Parts                                                                         by Weight                                             ______________________________________                                        (a) a block copolymer having at least two mono-                                   alkenyl arene polymer end blocks A and                                        at least one elastomeric conjugated diene mid                                 block B, each block A having an average                                       molecular weight between about 5,000 and                                                                       100                                          about 125,000 and each block B having an                                      average molecular weight between about                                        15,000 and about 250,000, said blocks                                         A comprising 8-65% by weight                                                  of the copolymer;                                                         (b) a polyarene produced by the anionic poly-                                     merization of a monoalkenyl arene;                                                                             20-90                                    (c) a hydrocarbon rubber extending oil; and                                                                        50-125                                   (d) a finely divided filler          0-250                                    ______________________________________                                    

wherein the ratio of the number average molecular weight of thepolyarene divided by the number average molecular weight of the A blockof the block copolymer is between about 0.6 and about 2.0 and the Qvalue of the polyarene is between about 1.0 and about 3.0.
 2. Acomposition according to claim 1 wherein said filler is selected fromthe group consisting of calcium carbonate, clay and silica.
 3. Acomposition according to claim 1 wherein said block copolymer isselectively hydrogenated such that no more than about 25% of thearomatic double bonds of block A are reduced by hydrogenation while atleast 75% of the aliphatic double bonds of block B are reduced byhydrogenation.
 4. A composition according to claim 1 including betweenabout 0 and about 150 parts by weight of a resin compatible with themonalkenyl arene end blocks, said resin being selected from the groupconsisting of polymers of alphamethyl styrene, copolymers of alphamethylstyrene and vinyltoluene, coumarone-indene resins, poly(indene) resins,poly-(methyl indene) resins and low molecular weight polystyrene resins.5. A composition according to claim 1 wherein the block copolymer has aformula A-B(B-A)_(n) where n varies from 1 to
 15. 6. A compositionaccording to claim 1 wherein said polyarene is formed by contacting amonoalkenyl arene with an organomonolithium initiator in a solution at atemperature of between about -60° F and about 300° F.
 7. A compositionaccording to claim 1 wherein said block A is a polystyrene block, saidblock B is a polybutadiene block and said polyarene is anionicpolystyrene.
 8. A composition according to claim 1 wherein the ratio ofthe number average molecular weight of the polyarene divided by thenumber average molecular weight of the A block of the block copolymer isbetween about 0.8 and about 1.5.
 9. A composition according to claim 1wherein the amount of polyarene varies from about 20 to about 90 partsby weight and the amount of hydrocarbon rubber extending oil varies fromabout 50 to about 125 parts by weight.